S1151G

特点

● 无铅兼容
不含卤素、锑、红磷等成分。废弃燃烧时不产生剧毒其他和残留有毒成分
UV Blocking/AOI兼容
高CTI,CTI≥600V
不适合翻洗绿油(阻焊油墨)


应用领域

汽车电子,如车载充电器OBC,充电桩等

建议用于8层以下,铜箔厚度<2 oz的通孔板

  • 产品性能
  • 产品证书
  • 资料下载
Items Method Condition Unit Typical Value
Tg IPC-TM-650 2.4.25 DSC 155
Td IPC-TM-650 2.4.24.6 5% wt. loss 380
CTE (Z-axis) IPC-TM-650 2.4.24 Before Tg ppm/℃ 36
After Tg ppm/℃ 220
50-260℃ % 2.8
T260 IPC-TM-650 2.4.24.1 TMA min >60
T288 IPC-TM-650 2.4.24.1 TMA min 30
Thermal Stress IPC-TM-650 2.4.13.1 288℃, solder dip -- pass
Volume Resistivity IPC-TM-650 2.5.17.1 After moisture resistance MΩ.cm 6.4 x 107
E-24/125 MΩ.cm 5.3 x 106
Surface Resistivity IPC-TM-650 2.5.17.1 After moisture resistance 4.8 x 107
E-24/125 2.8 x 106
Arc Resistance IPC-TM-650 2.5.1 D-48/50+D-4/23 s 140
Dielectric Breakdown IPC-TM-650 2.5.6 D-48/50+D-4/23 kV 45+kV NB
Dissipation Constant (Dk) IPC-TM-650 2.5.5.9 1MHz -- 4.8
IEC 61189-2-721 10GHz --
Dissipation Factor (Df) IPC-TM-650 2.5.5.9 1MHz -- 0.010
IEC 61189-2-721 10GHz --
Peel Strength (1Oz HTE copper foil) IPC-TM-650 2.4.8 A N/mm
After thermal Stress 288℃,10s N/mm 1.4
125℃ N/mm 1.3
Flexural Strength LW IPC-TM-650 2.4.4 A MPa 600
CW IPC-TM-650 2.4.4 A MPa 450
Water Absorption IPC-TM-650 2.6.2.1 E-1/105+D-24/23 % 0.10
CTI IEC60112 A Rating PLC 0
Flammability UL94 C-48/23/50 Rating V-0
E-24/125 Rating V-0

Remarks:

1. 626969cm澳门 the typical value is based on the 1.6mm specimen, while the Tg is for specimen≥0.50mm.

2. 626969cm澳门 the typical values listed above are for your reference only and not intended for specification. Please contact Shengyi Technology Co., Ltd. for detailed information. 626969cm澳门 rights from this data sheet are reserved by Shengyi Technology Co., Ltd.

Explanation: C=Humidity conditioning, D=Immersion conditioning in distilled water, E=Temperature conditioning

The first digit following the letter indicates the duration of preconditioning in hours, the second digit the preconditioning temperature in and the third digit the relative humidity.